MATERIAL DATA
Typical
Properties* |
Condition |
Units |
ASTM
Test Method |
U.S.
Conventional |
SI
Metric |
| Tensile Stress at Yield |
73 ° F |
6,100psi |
42MPa |
D 638 |
| Tensile Modulus |
73 ° F |
370,00psi |
2.56GPa |
D 638 |
| Elongation at Fail |
73 ° F |
30% |
D 638 |
| Flexural Stress at Yield |
73 ° F |
10,500psi |
72MPa |
D 790 |
| Flexural Modulus |
73 ° F |
380,000
psi |
206GPa |
D 790 |
| Load Impact, Notched |
73 ° F |
7.0
ft-lb/in |
375J/m |
D 256 |
| (1/8 X1/2 - in Bar) |
-40 ° F |
1.2
ft-lb/in |
64J/m |
|
| Rockwell Hardness |
73 ° F |
1.09 |
D 785 |
| Specific Gravity |
73 ° F |
1.05 |
D 792 |
| Deflection
Temperature Under Load (½ in X ½ in bar)
Unannealed
Annealed |
|
D 648 |
264 psi |
185 °
F |
85 ° C |
66 psi |
197 °
F |
92 ° C |
264 psi |
202 °
F |
94 ° C |
66psi |
211 °
F |
98 ° C |
| Vicat Softening
Temperature |
1 kg |
223 °
F |
106 ° C |
D
1525 |
| Melt Flow |
230/308 |
5.0 |
D
1238 |
| Coefficient of Linear
Expansion |
|
5.0 X 10-5 in/in/ ° F |
9.0
X 10-5
mm/mm/ ° C |
D
696 |
| UL Flame Class
Rating** |
0.062 in |
HB |
UL
94 |
|
0.125 in |
HB |
|
*These items are provided as general information only.
**Flammability results are based on small-scale laboratory tests for purposes of
relative comparison and are not untended to reflect the hazards presented by this or any
other material under actual fire conditions.
|
|
|
|